产品描述

牌号（Shop sign）: ZG-P-7165/ZG-I-7249

中低硬度、中低密度男女休闲鞋底原液

Medium and low-hardness and medium and low-density PU Resin for sole of casual shoes for both men and women

1. 特性：中低硬度，中低密度。

Characteristic: Medium and low hardness, medium and low density.

2. 用途：适用于男女休闲鞋中底的生产。

Application: Applicable to the production of medium soles of casual shoes for both men and women

3. 原液特性Typical properties of PU Resin

品名

Name of products

外观

Appearance

粘度Viscosity（Pa·s/50℃）

密度Density（g/cm³/40℃）

包装Package（kg）

ZG-P-7165

白色或淡黄，液状无异物White or pale yellow, liquid, no foreign material

0.50-1.00

1.16-1.20

ZG-I-7249

透明液体无异物Transparent liquid, no foreign material

0.10-0.30

1.18-1.20

参考发货配比(Reference shipments ratio)：A/B=30/23(桶)

Reference shipments ratio: A/B=30/23(barrel)

4. 成型条件及物性值(Molding conditions & physical properties)：

测试项目Test item	参考物性值Reference physical properties
鞋底成型密度Molded density of sole（g/cm³）	0.30~0.40
硬度(A型)Hardness (type A)	45~60
拉伸强度Tensile strength（MPa）	3.0~4.0
伸长率Elongation（％）	300~400
NBS耐磨NBS abrasion resistance（％）	≥10%
自由泡密度Free foam density（g/cm³）	0.20~0.25
耐折性(常温）(4万次裂口长度，mm)Folding endurance (room temperature)(40,000 gap length mm)	＜8

●配合比率是以最佳配比值为基础，此配比值会随添加的颜料助剂种类和添加量不同而变化。

Matching ratio is based on the optimal matching value which will vary with the category and additive amount of paint additives added.

●自由泡沫密度会依季节（温度，湿度）的不同而变化。

Free foam density will vary with the seasons (temperature, humidity).

●脱模时间会随成型品厚度的增加而延长。

Stripping time will be extended with the increase of the thickness of moldings.

●耐折条件：屈挠角度为 90度，频率为80次/min*4万次。

Folding endurance conditions: bending angle is 90 degrees and the frequency is 80 times / min * 40 thousand times

● 以上数据仅作参考，具体数据以实际操作为准。如需其他物性指标，请与我公司联系。

Data listed above is just for reference. The specific data is subjected to the practical operation. If other physical properties are required, please contact us.